NORYL GTX™ GTX979 resin

About
NORYL GTX979 is a conductive, high heat material. It is especially designed for in- and on-line painted bodypanels and fenders in particular, with conductivity for electro-static painting in an unique way.&&

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS+PA
Material Status	Commercial: Negative
Features	Conductive,Sprayable,High Heat Resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.08	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate
280℃，5.0kg	15	g/10min	ASTM D1238
Melt Volume Rate
280℃，5 kg	11.0	cm³/10min	ISO 1133
Shrinkage rate			Internal Method
MD：3.2 mm	1.2 to 1.6	%	Internal Method
TD：3.2 mm	1.2 to 1.6	%	Internal Method
Water absorption rate			ISO 62
Saturation, 23 ℃	4.2	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.2	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
—	2000	MPa	ASTM D638
—	2100	MPa	ISO 527-1-2
tensile strength
yield	55.0	MPa	ASTM D638
yield	55.0	MPa	ISO 527-2/50
fracture	50.0	MPa	ASTM D638
fracture	50.0	MPa	ISO 527-2/50
Tensile strain
yield	5.0	%	ASTM D638
yield	4.0	%	ISO 527-2/50
fracture	60	%	ASTM D638
fracture	30	%	ISO 527-2/50
Bending modulus
50 mm span	2050	MPa	ASTM D790
—	2150	MPa	ISO 178
bending strength
—	80.0	MPa	ISO 178
Yield, 50 mm span	80.0	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	12	kJ/m²	ISO 179/1eA
23℃	20	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
-30℃	150	J/m	ASTM D256
23℃	220	J/m	ASTM D256
-30℃	7.0	kJ/m²	ISO 180-1A
23℃	17	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	无断裂		ISO 180/1U
23℃	无断裂		ISO 180/1U
Dart impact equipped with measuring instruments
23℃，Total Energy	50.0	J	ASTM D3763

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed, 3.2 mm	185	℃	ASTM D648
0.45 MPa, unannealed, 100 mm span	178	℃	ISO 75-2/Be
Vicat Softening Temp
B50	180	℃	ASTM D1525 11 , ISO 306/B50 11
B120	182	℃	ISO 306/B120
Linear coefficient of thermal expansion
MD：-40~40℃	9.5E-5	1/℃	ASTM E831
MD：23~80℃	9.6E-5	1/℃	ISO 11359-2
TD：-40~40℃	1.0E-4	1/℃	ASTM E831
TD：23~80℃	9.6E-5	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+3 to 1.0E+4	ohms·cm	Internal Method

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Glowing wire flammability index
3.2 mm	650	℃	IEC 60695-2-12

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100 to 120	°C
Drying time	2.0 to 3.0	hr
Recommended maximum moisture content	0.070	%
Hopper temperature	60 to 80	°C
Barrel rear temperature	260 to 280	°C
Barrel middle temperature	280 to 300	°C
Barrel front temperature	290 to 320	°C
Nozzle temperature	280 to 310	°C
Processing (melt) temperature	290 to 320	°C
Mold temperature	80 to 120	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.