Asaflex™ 825

About
Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC, for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form. Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP laminate films and IC magazine rails, and with SC* for shrink films. * Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.&&

About

Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC*, for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form. Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP* laminate films and IC magazine rails, and with SC* for shrink films. * Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.&&

Product Description
Supplier	Asahi Kasei
Generic	SBS
Material Status	Commercial: Active
Features	Good Clarity,High impact resistance,Copolymer,Heat Stabilized
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ISO 1183
Melt Flow Rate
200℃，5.0kg	6.0	g/10min	ISO 1133
Shrinkage rate	0.20 to 0.80	%
Water absorption rate
23℃，24hr	0.10	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
Complete fracture	2.0	kJ/m²	ISO 179
Charpy Unnotch Impact strength
Complete fracture	100	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	57.0	℃	ISO 75-2/A
Vicat Softening Temp
A50	82.0	℃	ISO 306/A50

optical performance	Nominal value	Unit	Test method
Transmittance
2000 µm	90.0	%	ISO 3537
Haze
2000 µm	0.50	%	ISO 3537

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	71		ISO 868
Rockwell hardness
R-level	55		ISO 2039-2
tensile strength
yield	27.0	MPa	ISO 527-2/5
Tensile strain
fracture	200	%	ISO 527-2/5
Bending modulus	1200	MPa	ISO 178
bending strength	37.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.