| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Medium Viscosity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 11 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| saturated | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，80*10*3 | 70 | kJ/m² | ISO 180/1A |
| -23℃，80*10*3 | 12 | kJ/m² | ISO 180/1A |
| Notched impact strength of cantilever beam | |||
| 23℃，80*10*3 | NB | ISO 180/1U | |
| -23℃，80*10*3 | NB | ISO 180/1U | |
| Charpy Notched Impact Strength | |||
| 23℃，80*10*3 | 73 | kJ/m² | ISO 179/1eA |
| -23℃，80*10*3 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -23℃，80*10*3 | NB | ISO 179/1eU | |
| -23℃，80*10*3 | NB | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.46 MPa，120*10*4，sp=100mm | 136 | ℃ | ISO 75/Be |
| 1.8 MPa，120*10*4，sp=100mm | 125 | ℃ | ISO 75/Ae |
| Thermal conductivity coefficient | 0.2 | W/m/K | ISO 8302 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ISO 489 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min | 63 | MPa | ISO 527 |
| Fracture, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile strain | |||
| Yield, 50 mm/min | 6.0 | % | ISO 527 |
| Fracture, 50 mm/min | 110 | % | ISO 527 |
| Bending modulus | |||
| 1 mm/min | 2350 | MPa | ISO 527 |
| bending strength | |||
| 2 mm/min | 90 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |