| About |
|---|
| Thermally conductive mineral and glass fiber filled PA6, FR, compliant with ECO protocols, non-brominated, non-chlorinated&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Thermal conductivity,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.79 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.42 | % | ASTM D955 |
| TD：24 hrs | 0.58 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.23 | % | Internal Method |
| 23℃，24hr | 0.040 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 13300 | MPa | ASTM D638 |
| — | 13300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 98.0 | MPa | ASTM D638 |
| fracture | 110 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.3 | % | ASTM D638 |
| fracture | 1.3 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 12500 | MPa | ASTM D790 |
| — | 13000 | MPa | ISO 178 |
| bending strength | |||
| — | 186 | MPa | ISO 178 |
| Yield, 50 mm span | 167 | MPa | ASTM D790 |
| Fracture, 50 mm span | 176 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 2.4 to 27 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 30 | J/m | ASTM D256 |
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 330 | J/m | ASTM D4812 |
| 23℃ | 25 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 227 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 228 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.4 mm | 215 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 206 | ℃ | ISO 75-2/Af |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：40~120℃ | 4.1E-5 | 1/℃ | ASTM E831 |
| TD：40~120℃ | 8.5E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | |||
| — | 1.4 | W/m/K | ASTM E1461 |
| — | 1.8 | W/m/K | ASTM E1461 |
| — | 0.90 | W/m/K | ISO 22007-2 |
| — | 1.9 | W/m/K | ISO 22007-2 |
| Relative temperature index | 120 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric strength | |||
| 1 mm in oil | > 10 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1.10 GHz | 4.84 | ASTM ES7-83 | |
| Dissipation factor | |||
| 1.1 GHz | 9.9E-3 | ASTM ES7-83 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0-3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 750 | ℃ | IEC 60695-2-13 |
| 3 mm | 800 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 260 to 275 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 270 to 295 | °C | |
| Mold temperature | 85 to 100 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 20 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Internal Method |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Break |
| 8. 80*10*4 mm |
| 9. through-plane, 10*10*3 mm sample |
| 10. in-plane, 25*0.4 mm disc |
| 11. through-plane, 80*3 mm discs |
| 12. in-plane, 80*3 mm discs |
| 13. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |