| About |
|---|
| SABIC® LDPE 2102X0 is a Low Density Polyethylene natural resin typically used for the production of Medium/High Voltage power cable insulation using the direct peroxide addition. SABIC® LDPE 2102X0 is a non-additivated and non-stabilized LDPE. It exhibits very high cleanliness and consistent purity. Sufficient antioxidant should be added to meet specific ageing requirements. Application Peroxide cross-linkable insulation for Medium/High Voltage power cable.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High purity,Crosslinked,Foaming performance,Good melt strength,Low density |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.9 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 89.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 108 | ℃ | DIN 53765 |
| Crystallization peak temperature | |||
| DSC | 97.0 | ℃ | |
| Fusion heat | 110 | J/g | DIN 53765 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 8.5E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | > 30 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 2.20 | ASTM D150 | |
| Dissipation factor | |||
| 60 Hz | 5.0E-4 | ASTM D150 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 45 | ISO 868 | |
| Tensile modulus | 175 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 9.00 | MPa | ISO 527-2 |
| fracture | 13.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 850 | % | ISO 527-2 |
| Elastic modulus | 250 | MPa | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2000 V/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |