| About |
|---|
| AMPLIFY™ TY 1355 Functional Polymer is a maleic anhydride (MAH) grafted LDPE polymer. AMPLIFY TY 1355 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide, EVOH and other polar substrates. Main Characteristics: Excellent adhesion to polyamide and EVOH High melt strengthFully formulated (does not have to be diluted with other polymers) for Extrusion Coating and Extrusion Lamination applications Complies with: US FDA 21 CFR 175.105 (c)(5) Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | 马来酸酐接枝共聚物 |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 | g/10min | ASTM D1238，ISO 1133 |
| MAH grafting level | Low | Internal Method | |
| Melt flow ratio | |||
| I10/12 | 10.0 | ASTM D1238 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 92.8 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 126 | ℃ | Internal Method |
| Crystallization peak temperature | |||
| DSC | 111 | ℃ | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |