| About |
|---|
| Description Light diffusion, Medium Impact Application (LED) Lamp Cover, Signboard, Lighting Decoration of Electronic Device&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS transparent |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃，3.2mm | 64 | J/m | ASTM D256 |
| 23℃，6.4mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 84.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 8.4E-5 | 1/℃ | ASTM D696 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | |||
| Fracture, 3.20 mm | 53.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 20 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2750 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 88.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel rear temperature | 190 to 210 | °C | |
| Barrel middle temperature | 200 to 220 | °C | |
| Barrel front temperature | 220 to 250 | °C | |
| Nozzle temperature | 230 to 250 | °C | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 0.981 to 3.92 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel 1 zone temperature | 190 to 210 | °C | |
| Barrel 2 zone temperature | 200 to 230 | °C | |
| Barrel 3 zone temperature | 210 to 240 | °C | |
| Barrel 4 zone temperature | 220 to 250 | °C | |
| Connector temperature | 220 to 250 | °C | |
| Melt temperature | 230 to 250 | °C | |
| Nozzle temperature | 220 to 250 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |