| PM 9630 Phenolic is a single stage glass fiber, and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stability with excellent electric insulation property and good heat resistance and machine ability. Typical applications include coil bobbins, switches and brush holders. JIS Type HM-R&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High Heat Resistance,Insulation,V-0 |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.82 | g/cm³ | JIS K6911 |
| Apparent density | 0.41 | g/cm³ | JIS K6911 |
| Shrinkage rate | |||
| MD: Transfer molding | 0.40 | % | JIS K6911 |
| Water absorption rate | |||
| 24hr | 0.20 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 186 | MPa | JIS K6911 |
| compressive strength | 274 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.8 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 260 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 13 | kV/mm | JIS K6911 |
| insulation resistance | JIS K6911 | ||
| — | 1.0E+11 | ohms | JIS K6911 |
| — | 1.0E+12 | ohms | JIS K6911 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 V/sec |
| 3. Before Boiling |
| 4. After Boiling |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |