| STYCAST 3050 Catalyst 9 is designed for potting and encapsulation applications with very small physical spacing between parts. The filler system is non-abrasive and readily machinable. This is a consideration when using a dispensing equipment or where subsequent machining of the cured part is required. STYCAST 3050 can be used with a variety of catalysts. For more information on mixed properties when used with other available catalysts, please contact your local technical service representative for assistance and recommendations. Product Benefits Very low viscosity Excellent penetration into tightly packed assemblies Good machinability General purpose Room temperature cure Good chemical resistance Good physical strength&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low Viscosity,Machinable,Baking,Solvent resistance,Room Temperature Cure |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD | 0.30 | % | ASTM D2566 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 54.0 | MPa | ASTM D412 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.40 | W/m/K | ASTM D2214 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 25 ℃ | 5.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 16 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 4.20 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.040 | ASTM D150 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| working temperature | -40 to 130 | ℃ |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Mix Ratio (PBW) | |||
| Hardener | 7.5 | ||
| Volume Mixing Ratio (PBV) | |||
| Resin | 100 | ||
| Hardener | 12 | ||
| Density | |||
| — | 1.54 | g/cm³ | |
| — | 1.61 | g/cm³ | |
| viscosity | |||
| — | 0.093 | Pa·s | |
| — | 0.60 | Pa·s | |
| — | 2.0 | Pa·s | |
| Curing time | |||
| 65℃ | 1.0 to 2.0 | hr | |
| 45℃ | 4.0 to 6.0 | hr | |
| 25℃ | 16 to 24 | hr | |
| storage stability | |||
| 25 ℃ | 45 | min | |
| Storage period | |||
| 25℃ | 6 | month |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 88 | ASTM D2240 | |
| bending strength | 75.0 | MPa | ASTM D790 |
| compressive strength | 144 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mixed |
| 3. Part A |
| 4. Part B |
| 5. 100 g mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |