| Nanocomposite based on a ABS/PA-Blend for high dimensional stability&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | ABS+PA |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | |
| Melt Volume Rate | |||
| 250℃，5 kg | 4.00 | cm³/10min | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 15 | kJ/m² | |
| 23℃ | 30 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 97.0 | ℃ | |
| 1.8 MPa, unannealed | 77.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 194 | ℃ | |
| — | 116 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | 27 | mm/min | |
| Flammability level | |||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| Glowing wire flammability index | |||
| 1.5 mm | 650 | ℃ | |
| 3.0 mm | 650 | ℃ | |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 675 | ℃ | |
| 3 mm | 675 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 85.0 | MPa | |
| Tensile modulus | 2400 | MPa | |
| tensile strength | |||
| yield | 39.0 | MPa | |
| Tensile strain | |||
| yield | 3.0 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |