| LUVOCOM® 3F PEEK 9581 NT is a Polyetheretherketone (PEEK) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for 3d printing, fused filament fabrication (fff) or extrusion. Important attributes of LUVOCOM® 3F PEEK 9581 NT are: Flame Rated Chemical Resistant Flame Retardant High Stiffness High Strength Typical applications include: Aerospace Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Flame Characteristics,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 380℃，10 kg | 22.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| 3.0 mm | 1.4 to 1.6 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3800 | MPa | ISO 527-2 |
| tensile strength | 97.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2 |
| Bending modulus | 3400 | MPa | ISO 178 |
| bending strength | 145 | MPa | ISO 178 |
| Bending strain | 7.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 7.0 | kJ/m² | |
| 23℃ | 7.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 190 | kJ/m² | |
| 23℃ | 190 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 145 | ℃ | ISO 75-2/A |
| Continuous use temperature | 250 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+12 | ohms | IEC 60093 |
| insulation resistance | > 1.0E+12 | ohms | IEC 60167 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Barrel 1 zone temperature | 360 to 370 | °C | |
| Barrel 2 zone temperature | 380 to 390 | °C | |
| Barrel 3 zone temperature | 390 to 400 | °C | |
| Melt temperature | 390 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |