| About |
|---|
| PPE+PS blend. 30% Glass reinforced. Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 3.2 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 2.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.10 to 0.40 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.10 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 8600 | MPa | ASTM D638 |
| — | 8200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 130 | MPa | ASTM D638 |
| fracture | 110 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| fracture | 2.5 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 7200 | MPa | ASTM D790 |
| — | 6800 | MPa | ISO 178 |
| bending strength | |||
| — | 160 | MPa | ISO 178 |
| Yield, 50 mm span | 160 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 120 | J/m | ASTM D256 |
| 23℃ | 100 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 590 | J/m | ASTM D4812 |
| 23℃ | 30 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 20.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 147 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 139 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 139 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 147 | ℃ | ASTM D1525 10 |
| B120 | 149 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.1E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 2.3E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.5E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 265 to 315 | °C | |
| Barrel middle temperature | 275 to 320 | °C | |
| Barrel front temperature | 290 to 325 | °C | |
| Nozzle temperature | 300 to 325 | °C | |
| Processing (melt) temperature | 300 to 325 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |