| Kangxi® PP-30GF is a Polypropylene product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Applications of Kangxi® PP-30GF include appliances and automotive. Characteristics include: Flame Rated Good Aesthetics Good Dimensional Stability Heat Resistant High Strength&& |
| Product Description | |
|---|---|
| Supplier | Kangxi |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Good Dimensional Stability,High Heat Resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.30 | % | ASTM D955 |
| TD | 1.0 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 160 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 150 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weathering resistance | |||
| 24 hrs，23℃ | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | 75.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.5 | % | ASTM D638 |
| Bending modulus | 5000 | MPa | ASTM D790 |
| bending strength | 90.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 180 to 230 | °C | |
| Barrel middle temperature | 180 to 230 | °C | |
| Barrel front temperature | 180 to 230 | °C | |
| Processing (melt) temperature | 220 to 245 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 0.39 in/min |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |