| About |
|---|
| EMERGE™ PC 4350 Advanced Resin is a polycarbonate resin offering ultraviolet light stability, high heat resistance and maximum toughness. This UV stable resin is available in a full range of colors that can be customer tailored to meet your product requirements. Applications: Appliances Outdoor applications Automotive components&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good flexibility,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 850 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23 ℃, 3.2 mm, injection molding | 无断裂 | ASTM D256 | |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, 3.20 mm, injection molding, total energy | 87.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed | 143 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 127 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 140 | ℃ | ASTM D648 |
| Vicat Softening Temp | 148 | ℃ | ASTM D1525 3 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.8E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 118 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm, injection molded | 2410 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 60.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 71.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 6.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 150 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2410 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 96.5 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 271 to 288 | °C | |
| Mold temperature | 66 to 99 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |