| About |
|---|
| Eastman Tritan™ LX150HF is a high flow grade of an amorphous copolyester with excellent appearance and clarity. Eastman Tritan™ LX150HF has viscosity reductions of 40-50% relative to standard grades of Eastman Tritan™. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. Tritan™ LX150HF was developed for the cosmetic, fragrance, and personal care markets. Tritan™ LX150HF can easily be converted into articles for application in consumer and personal care markets by injection molding, extrusion blow molding, and injection blow molding.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility,High impact resistance,High liquidity,Hydrolysis stability,Quick molding cycle,High Heat Resistance,Solvent resistance,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | No Break | ASTM D256 | |
| 23℃ | No Break | ASTM D256 | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，Energy at Peak Load | 57.0 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 53.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 94.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1580 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 52.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 43.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 210 | % | ASTM D638 |
| Yield, 23 ℃ | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1580 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 23 ℃ | 64.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| -40℃ | 110 | J/m | ASTM D256 |
| 23℃ | 860 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 282 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |