SABIC® HDPE BM6246LS

About
SABIC® HDPE BM6246LS is a high density polyethylene blow moulding grade for high rigidity, good toughness and good processability. These properties offer bottles to be made at lower weight with very good top load strength. Typical applications. SABIC® HDPE BM6246LS is typically used for blow moulding bottles for packaging organoleptically sensitive products, e.g. milk, fruit juice and other dairy products. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE BM6246LS is a high density polyethylene blow moulding grade for high rigidity, good toughness and good processability. These properties offer bottles to be made at lower weight with very good top load strength. Typical applications. SABIC® HDPE BM6246LS is typically used for blow moulding bottles for packaging organoleptically sensitive products, e.g. milk, fruit juice and other dairy products. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good flexibility,High density
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.961	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.70	g/10min
190℃，21.6kg	46	g/10min
190℃，5.0kg	2.5	g/10min
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, molded, F50	15.0	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/A
-30 ℃, molded	7.0	kJ/m²
23 ℃, molded	13	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	88.0	℃	ISO 75-2/B
Vicat Softening Temp	129	℃	ISO 306/A
Melting temperature
DSC	134	℃	ISO 11357-3
Enthalpy Change	223	J/g	ISO 11357-3

Supplementary information	Nominal value	Unit	Test method
Blow molding barrel temperature	175 to 200	℃
Blow Molding Melt Temperature	205	℃

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	63		ISO 868
Tensile modulus
2 mm, molded into shape	1250	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	29.0	MPa
Fracture, 2 mm, molded	18.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 1000	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1550	MPa	ISO 178
bending strength
2 mm, molded into shape	31.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.