| ALTECH® PP-H A 2030/159 GF30 CP BK1090-13LWT is a Polypropylene Homopolymer (PP Homopolymer) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include: Flame Rated RoHS Compliant Chemically Coupled Heat Stabilizer High Stiffness&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Chemical coupling,Heat Stabilized,Homopolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 2.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 2.40 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 50 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 30 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 140 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 163 | ℃ | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 750 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 85.0 | MPa | ISO 2039-1 |
| Tensile modulus | 5500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 75.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | 5000 | MPa | ISO 178 |
| bending strength | 100 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 to 120 | °C | |
| Hot air dryer | 80 to 120 | °C | |
| Drying time | |||
| Desiccant desiccant | 2.0 to 4.0 | hr | |
| Hot air dryer | 2.0 to 3.0 | hr | |
| Processing (melt) temperature | 200 to 270 | °C | |
| Mold temperature | 20 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |