| DIOFAN® A 736 is a PVDC latex recommended for use as a flexible underlayer for barrier coating on rigid PVC or PVC/ PE film, to be covered with DIOFAN® 193 D as top coat. The film structure is used for blister application in pharmaceutical packaging.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDC |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low odor,Moisture resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| PH value | Acidic | ||
| surface tension | |||
| Foaming trend | 46 | mN/m | |
| Film-forming property | |||
| Minimum film-forming temperature | 17 | ℃ | |
| Solid content | 60 | % | |
| Density | |||
| Disperse (wet) | 1.330 | g/cm³ | |
| coating | 1.650 | g/cm³ | |
| Lotion type | 阴离子 | ||
| viscosity | |||
| 20℃ | 0.02 | Pa·s | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen transfer rate | |||
| 25℃，85% RH，1.0 µm | 21 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 38℃，90% RH，1.0 µm | 18 | g/m²/24 hr | ASTM F1249 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | 500 | kJ/m² |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Shelf life – Latex | |||
| 23℃ | 12 | month | |
| Steel ball drop test | > 900 | mm |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Coating properties: 40 g/m² PVDC coating on PVC 250 µm stored 6 months at 23 °C, 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |