| PBT+PET含有30%玻纤增强材料，模具释放，热稳定，可用于食品接触 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 5 mm/min | |||
| 5 mm/min | |||
| Tensile strain | |||
| yield | 101 | MPa | ASTM D 638 |
| 5 mm/min | |||
| fracture | 107 | MPa | ASTM D 638 |
| 5 mm/min | |||
| Tensile modulus | |||
| 5 mm/min | 8150 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 50 mm span | 173 | MPa | ASTM D790 |
| yield | 2.5 | % | ASTM D 638 |
| fracture | 2.5 | % | ASTM D 638 |
| Bending modulus | |||
| 7130 | MPa | ASTM D790 | |
| Tensile modulus | |||
| 1 mm/min | 9000 | MPa | ISO 527 |
| bending strength | |||
| Yield, 2 mm/min | 200 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 8000 | MPa | ISO 178 |
| yield | 140 | MPa | ISO 527 |
| fracture | 140 | MPa | ISO 527 |
| yield | 2.5 | % | ISO 527 |
| fracture | 2.5 | % | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 80 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 640 | J/m | ASTM D4812 |
| Instrument control anti impact total energy 23 ℃ | 71 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 200 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 202 | ℃ | ISO 75/Ae |
| 1.8 MPa, unannealed, 3.2 mm | 195 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.5E-05 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.E-05 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 2.5E-05 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 8.1E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp | |||
| B50 | 200 | ℃ | ISO 306 |
| B120 | 205 | ℃ | ISO 306 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.15 | % | ISO 62 |
| Saturation, 23 ℃ | 0.15 | % | ASTM D570 |
| 23℃，50% RH | 0.06 | % | ISO 62 |
| 23℃，50% RH | 0.06 | % | |
| Shrinkage rate | |||
| MD：3.2 mm | 0.3-0.8 | % | Internal Method |
| Melt Flow Rate | |||
| 265℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，2.16 kg | 13 | cm³/10min | ISO 1133 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying temperature | 110-120 | °C | |
| Drying time | 4-6 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 260-285 | °C | |
| Nozzle temperature | 265-275 | °C | |
| Front temperature | 260-280 | °C | |
| Mid section temperature | 255-280 | °C | |
| Post stage temperature | 240-260 | °C | |
| Hopper temperature | 40-60 | °C | |
| Mold temperature | 60-110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |