| About |
|---|
| This high molecular weight, hexene copolymer is tailored for blown film applications that require: Soft feel Good toughness, impact strength and tear resistance Good blending characteristics with HDPE HMW resins Typical applications for HHM TR-131 include: T-shirt bags Shopping bags Trash bags&& |
| Product Description | |
|---|---|
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Food contact compliance,High molecular weight,Good tear strength,Copolymer,Soft,Hexene copolymers |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | > 1000 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| Tangent, molded | 760 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| tensile strength | ASTM D882 | ||
| MD, yield, 25 µ m, blow molded film | 21.0 | MPa | |
| TD, yield, 25 µ m, blow molded film | 23.0 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m, blow molded film | 500 | % | |
| TD, fracture, 25 µ m, blow molded film | 660 | % | |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 170 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 30 | g | |
| TD: 25 µ m, blow molded film | 350 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.50 in/min |
| 3. 16:1 span:depth |
| 4. 2.0 in/min |
| 5. 66 cm |
| 6. Type I specimen |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |