| Product Description | |
|---|---|
| Supplier | Techno |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.9 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 88.0 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 108 | ISO 2039-2 | |
| tensile strength | |||
| yield | 46.0 | MPa | ISO 527-2 |
| Bending modulus | 2410 | MPa | ISO 178 |
| bending strength | 73.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 85 to 95 | °C | |
| Drying time | 2.0 to 5.0 | hr | |
| Temperature at the rear of the barrel | 220 to 270 | °C | |
| Temperature in the middle of the barrel | 220 to 270 | °C | |
| Front temperature of material barrel | 220 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |