| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| 24hr | 0.06 | % | ASTM D570 |
| Density | 1.11 | ASTM D792 | |
| Shrinkage rate | |||
| 3.2 mm | 0.5 – 0.7 | % | Internal Method |
| Shrinkage of the mold on the stretching rod | |||
| transverse | 0.5 – 0.7 | % | SABIC Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Type I, 50 mm/min | |||
| yield | 76 | MPa | ASTM D 638 |
| fracture | 56 | MPa | ASTM D 638 |
| Tensile strain | |||
| Yield, Type I, 50 mm/min | 9.5 | % | ASTM D638 |
| Fracture, Type I, 50 mm/min | 18 | % | ASTM D638 |
| bending strength | |||
| Yield, 2.60 mm/min, 100 mm span | 113 | MPa | ASTM D790 |
| Bending modulus | |||
| 2.60 mm/min, 100 mm span | 2690 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃ | |||
| No gap | 114 | cm-kgf/cm | ASTM D 4812 |
| Gap | 16 | cm-kgf/cm | ASTM D 256 |
| Impact energy of the instrument @ peak value | |||
| 23℃ | 428 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 150 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 133 | ℃ | ASTM D648 |
| 1.8 MPa | 122 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Electrical performance | 110 | ℃ | UL 746B |
| Impact mechanical performance | 105 | ℃ | UL 746B |
| Non mechanical impact performance | 110 | ℃ | UL 746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.E+16 | ohms·cm | ASTM D257 |
| Surface resistivity | >1.E+16 | ohms/sq | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 18.8 | kV/mm | ASTM D149 |
| Relative permittivity | |||
| 50-60 Hz | 2.57 | ASTM D150 | |
| 1 MHz | 2.49 | ASTM D150 | |
| Dissipation factor | |||
| 50-60 Hz | 0.0052 | ASTM D150 | |
| 1 MHz | 0.0026 | ASTM D150 | |
| Arc resistance | |||
| Tungsten wire | 6 | PLC Code | ASTM D495 |
| Hot wire ignition | |||
| PLC | 0 | PLC Code | UL 746A |
| High voltage arc tracking rate {PLC} | 4 | PLC Code | UL 746A |
| High current arc ignition (surface {PLC}) | 0 | PLC Code | UL 746A |
| Comparison tracking index | |||
| UL{PLC} | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 94V-0 flame level | 0.76 | mm | UL 94 |
| ultraviolet radiation | |||
| Water exposure/soaking | F2 | UL 746C |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |