Amodel® A-6135 HS

About
Amodel® A-6135 HS polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HS resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Natural A-6135 HS NT&&

About

Amodel® A-6135 HS polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HS resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Natural A-6135 HS NT&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good liquidity,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.45	g/cm³
Shrinkage rate
MD	0.60	%
TD	0.90	%
TD	1.0	%
MD	0.50	%
Water absorption rate
24hr	0.30	%
23℃，24hr	0.29	%

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	9.2	kJ/m²
Charpy Unnotch Impact strength
23℃	60	kJ/m²
Impact strength of cantilever beam notch
—	85	J/m
23℃	9.1	kJ/m²
Notched impact strength of cantilever beam
—	800	J/m
23℃	62	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	303	℃
1.8 MPa, unannealed	288	℃
1.8 MPa, annealed, 3.2 mm	291	℃
Melting temperature	310	℃
Linear coefficient of thermal expansion
MD：0~100℃	2.2E-5	1/℃
MD：100~200℃	1.6E-5	1/℃
TD：0~100℃	6.1E-5	1/℃
TD：100~200℃	1.0E-4	1/℃

MECHANICAL	Nominal value	Unit
Rockwell hardness
R-level	125
Tensile modulus
—	13800	MPa
23℃	11500	MPa
100℃	7310	MPa
150℃	6270	MPa
175℃	5310	MPa
tensile strength
Fracture, 23 ℃	211	MPa
Fracture, 100 ℃	121	MPa
Fracture, 150 ℃	92.4	MPa
Fracture, 175 ℃	82.0	MPa
—	203	MPa
Tensile strain
fracture	1.9	%
Fracture, 23 ℃	2.0	%
Fracture, 100 ℃	4.3	%
Fracture, 150 ℃	4.9	%
Fracture, 175 ℃	4.7	%
Bending modulus
—	11400	MPa
23℃	11400	MPa
100℃	6600	MPa
150℃	4900	MPa
175℃	4600	MPa
bending strength
—	310	MPa
3.50% strain, 23 ℃	300	MPa
3.50% strain, 100 ℃	170	MPa
3.50% strain, 150 ℃	123	MPa
3.50% strain, 175 ℃	112	MPa
compressive strength	148	MPa
shear strength	87.6	MPa
Poisson’s ratio	0.39

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.030 to 0.060	%
Barrel rear temperature	316 to 321	°C
Barrel front temperature	327 to 332	°C
Processing (melt) temperature	321 to 335	°C
Mold temperature	66 to 93	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.