| About |
|---|
| Description JH-330B is high impact block copolymer with high ethylene content as co-monomer. This grade is designed to be processed in conventional Injection molding equipment. JH-330B shows extremely high impact resistance at low temperature and has also low blush characteristic. JH-330B contains UV stabilizer. Applications Crate, Pallet Safety Block, Toy, General Merchandise etc.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Blush resistance,High impact resistance,Block Copolymer,low-temperature impact resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| 4.0 | g/10min | ISO 1133 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 22.6 | MPa | ASTM D638 |
| yield | 22.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| — | 1130 | MPa | ASTM D790 |
| — | 880 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -10℃ | 64 | J/m | ASTM D256 |
| -10℃ | 59 | J/m | ISO 180 |
| 23℃ | 290 | J/m | ASTM D256 |
| 23℃ | 270 | J/m | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |