| About |
|---|
| Toraycon® 1100M is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific or Europe. Primary attribute of Toraycon® 1100M: RoHS Compliant.&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.0kg | 31 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 59.0 | cm³/10min | ISO 1133 |
| Viscosity value | |||
| 0.5% OCP | 85.0 | cm³/g | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 60.0 | MPa | ISO 527-2 |
| yield | 57.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 32 | % | ISO 527-2 |
| fracture | 27 | % | ASTM D638 |
| Bending modulus | 2500 | MPa | ASTM D790 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 84.0 | MPa | ASTM D790 |
| bending strength | 87.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.4 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 36 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 224 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Intrinsic Viscosity under phenol/dichlorobenzen method, 1050M = 0.77 dl/g, 1100M = 0.83dl/g, 1200M = 1.08dl/g. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |