| Provisional – PP Homopolymer for Raffia applications PP 506P is intended for producing low denier stretched tapes with following features. Consistent processability Good processability at high line speeds and low deniers Low tapes shrinkage Low water carry over Very good mechanical properties Typical Applications PP 506P can be used for producing carpet backing, woven bags, cable fillers, geotextiles and concrete reinforcements.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low contractility,Low water portability,Homopolymer |
| Availabilitys | North America,Latin America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.8 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 32 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ASTM D648 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | |||
| Yield, injection molding | 35.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, injection molding | 12 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, injection molding | 1500 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 235 to 250 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 235 to 250 | °C | |
| Processing (melt) temperature | 250 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. Rate B (120°C/h) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |