Quadrant EPP Nylatron® 703 XL

About
Quadrant EPP Nylatron® 703 XL is a Polyamide 6 (Nylon 6) product. It can be processed by casting and is available in Latin America or North America. Characteristics include: Flame Rated Conductive Wear Resistant&&

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	4	kJ/m²	ISO 179-1/eA
Charpy Unnotch Impact strength	25	kJ/m²	ISO 179-1/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa	70	℃	ISO 75-1/-2
Maximum operating temperature
short time	160	℃
Continuous: 5000hr	105	°C
Continuous: 20000hr	90	°C
Melting temperature
DSC，10℃/min	215	℃	ISO 11357-1/-3
Linear coefficient of thermal expansion
MD
23 to 60 ℃	8.5E-5	m/(m·K)
23 to 100 ℃	1.0E-4	m/(m·K)
Thermal conductivity coefficient
23℃	0.30	W/m/K
Minimum operating temperature	-20	℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity
23℃	> 1.0E+13	ohm/sq	IEC 60093
23°C，50%RH	> 1.0E+12	ohm/sq	IEC 60093
Volume resistivity
23℃	> 1.0E+14	ohm·cm	IEC 60093
23°C，50%RH	> 1.0E+12	ohm·cm	IEC 60093

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
3.0mm	HB		UL 94
6.0mm	HB		UL 94
Oxygen index	＜20	%	ISO 4589-1/-2

MECHANICAL	Nominal value	Unit	Test method
Tensile stress
23 ℃, 50 mm/min, yield	60	MPa	ISO 527-1/-2
23 ℃, 50% RH, 50 mm/min, yield	40	MPa	ISO 527-1/-2
tensile strength
23℃，50 mm/min	60	MPa	ISO 527-1/-2
Tensile strain
23 ℃, 50 mm/min, yield	6	%	ISO 527-1/-2
23 ℃, 50 mm/min, fracture	15	%	ISO 527-1/-2
23 ℃, 50% RH, 50 mm/min, yield	＞25	%	ISO 527-1/-2
Tensile modulus
23℃，1 mm/min	2750	MPa	ISO 527-1/-2
23℃，50%RH，1 mm/min	1350	MPa	ISO 527-1/-2
compressive strength
23 ℃, 1% strain	26	MPa	ISO 604
23 ℃, 2% strain	48	MPa	ISO 604
23 ℃, 5% strain	69	MPa	ISO 604
Ball hardness
10.0 mm	120	N/mm²	ISO 2039-1
Rockwell hardness
R-grade, 10.00 mm	109		ISO 2039-2
M-grade, 10.00 mm	59		ISO 2039-2

Notes
1. Typical properties: these are not to be construed as specifications.
2. 1-10, 1=Easier to Machine
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.