| About |
|---|
| Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties. Main applications: corrosion protection in the chemical industry, coating (painting, co-extrusion), off-shore, wire and cable, PPA, Battery. Kynar® ADX 111 resin allows primer less powder coating (direct adhesion to metals after standard surface preparation. Can be used easily in standard application processes: Dip coating in fluidized bed Electrostatic spraying Hot flocking&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PVDF |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,High purity,Sprayable,Block resin,Solvent resistance,Heat Stabilized,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.78 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 27.0 | cm³/10min | ISO 1133 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.070 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 54.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 132 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Glass transition temperature | -40.0 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 139 | ℃ | ISO 306 |
| Melting temperature | 169 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 2.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 21 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 9.00 | IEC 60250 | |
| 1 MHz | 7.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.032 | IEC 60250 | |
| 1 MHz | 0.21 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Flammability level | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.8 mm | V-0 | ||
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| Extreme oxygen index | 44 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |