| About |
|---|
| TAISOX® 8050 is a High Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of TAISOX® 8050 are: Good Processability Impact Resistant Rigid Typical applications include: Containers Seating&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,High density |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | 137 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 |
| Melting temperature | 135 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 30.4 | MPa | ASTM D638 |
| fracture | 23.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1000 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 170 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |