| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | ISO 2577 | ||
| TD：150x105x3，4hrs | 0.50 | % | ISO 2577 |
| MD：150x105x3，4 hrs | 0.50 | % | ISO 2577 |
| Melt Flow | |||
| 260℃，5kg | 9.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 194 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| 23℃ | 8500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 107 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.3 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 8000 | MPa | ISO 178-A |
| bending strength | ISO 178/A | ||
| Yield, 23 ℃ | 180 | MPa | ISO 178-A |
| Fracture, 23 ℃ | 3.0 | % | ISO 178/A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 180/1U |
| Impact strength of cantilever beam notch | |||
| -30℃ | <=10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 35 | kJ/m² | ISO 180/1U |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 30 | % | ISO 4589-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 168 | ℃ | ISO 75-1/2 |
| 0.45 MPa, unannealed | 205 | ℃ | ISO 75-1/2 |
| Melting temperature | |||
| 10℃ / min | 223 | ℃ | ISO 11357-3/-1 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 4.0E-5 | 1/℃ | ISO 11359-1/-2 |
| MD：23~55℃ | 6.0E-5 | 1/℃ | ISO 11359-1/-2 |
| Solution temperature | 290 | ℃ | |
| Mold temperature | 80 | ℃ |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |