| Polypropylene PPC 3640 is a nucleated heterophasic copolymer with a Melt Flow Index of 1.3 g/10 min. Polypropylene PPC 3640 is characterized by improved stiffness, creep resistance and high impact resistance. Polypropylene PPC 3640 has been developed specifically for the extrusion of corrugated cardboard, corrugated and twin walled pipes, conduit pipe and other extrusion applications.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Nucleation,Impact copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent density | 0.53 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.3 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 8.0 | kJ/m² | ISO 179 |
| 23℃ | > 50 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -20℃ | 7.0 | kJ/m² | ISO 180 |
| 23℃ | > 50 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 52.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 150 | ℃ | ISO 306/A50 |
| B50 | 75.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 165 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 82 | ISO 2039-2 | |
| Tensile modulus | 1350 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 27.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2 |
| Bending modulus | 1300 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |