Kynar® 720 Black

About
KYNAR® 720 BLACK is a semi-crystalline low molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply a grade suitable for a variety of processing requirements and end-use applications. KYNAR® 720 BLACK is recommended for fine extrusion operations. It is also suitable for injection molding applications where very thin cross-sections for intricate design require excellent melt flow characteristics.&&

About

KYNAR® 720 BLACK is a semi-crystalline low molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply a grade suitable for a variety of processing requirements and end-use applications. KYNAR® 720 BLACK is recommended for fine extrusion operations. It is also suitable for injection molding applications where very thin cross-sections for intricate design require excellent melt flow characteristics.&&

Product Description
Supplier	Arkema
Generic	PVDF
Material Status	Commercial: Active
Features	Good liquidity,Hypocrystalline,Low molecular weight
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 23 ℃	76 to 80		ASTM D2240
tensile strength
Fracture, 23 ℃	34.5 to 55.2	MPa	ASTM D638
Yield, 23 ℃	44.8 to 55.2	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	20 to 100	%	ASTM D638
Bending modulus
23℃	1380 to 2310	MPa	ASTM D790
bending strength
23℃	58.6 to 75.8	MPa	ASTM D790
compressive strength
23℃	68.9 to 103	MPa	ASTM D695

THERMAL	Nominal value	Unit	Test method
Melting peak temperature	165 to 172	℃	ASTM D3418

Electrical performance	Nominal value	Unit	Test method
Volume resistivity
20 ℃	2.0E+14	ohms·cm	ASTM D257

PHYSICAL	Nominal value	Unit	Test method
Density	1.77 to 1.79	g/cm³	ASTM D792
Melt Flow Rate	5.0 to 27	g/10min	ASTM D1238
Apparent viscosity of melt
232℃，100 sec^-1	600 to 1200	Pa·s	ASTM D3835

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.