| About |
|---|
| TAISOX® 8003H is a High Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for blow molding. Important attributes of TAISOX® 8003H are: Chemical Resistant Good Stiffness Impact Resistant Rigid Typical applications include: Bottles Consumer Goods Containers Medical/Healthcare Tanks&& |
| Product Description | |
|---|---|
| Supplier | fpc-tw |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High density,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 134 | ℃ | ASTM D4591 |
| Vicat Softening Temp | |||
| 127 | ℃ | ASTM D1525 | |
| Embrittlement temperature | -70.0 | ℃ | ASTM D746 |
| Linear coefficient of thermal expansion |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 69 | ASTM D2240 | |
| tensile strength | |||
| 23℃ | 30.40 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1000 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |