| About |
|---|
| Description Blow Molding, Heat Resistance Application Automotives Exterior Housing (Spoiler,Bumper Guard etc.)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 88 | J/m | |
| -30℃，6.4mm | 78 | J/m | |
| 23℃，3.2mm | 260 | J/m | |
| 23℃，6.4mm | 250 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 103 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 97.0 | ℃ | |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 101 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 45.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 15 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2160 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 71.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Connector temperature | 220 | °C | |
| Melt temperature | 200 to 210 | °C | |
| Nozzle temperature | 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |