| 25% Methyl Acrylate&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EMA |
| Material Status | Commercial: Active |
| Features | Good flexibility,Copolymer,Soft,High ESCR |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.944 | g/cm³ | ASTM D1505 |
| Density | 0.944 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.60 | g/10min | ASTM D1238 |
| 190℃，2.16kg | 0.60 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 78 | ASTM D2240 | |
| Shaw’s D | 19 | ASTM D2240 | |
| Shore hardness | ISO 868 | ||
| Shaw’s A | 78 | ISO 868 | |
| Shaw’s D | 19 | ISO 868 | |
| Tensile modulus | 19.0 | MPa | ASTM D638 |
| Tensile modulus | 19.0 | MPa | ISO 527-1-2 |
| tensile strength | 14.0 | MPa | ASTM D638 |
| yield | 14.0 | MPa | ISO 527-2/500 |
| Tensile strain | |||
| fracture | 860 | % | ASTM D638 |
| fracture | 860 | % | ISO 527-2/500 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 45.0 | ℃ | ASTM D1525 4 |
| A50 | 45.0 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 90.0 | ℃ | ISO 3146 |
| Melting temperature | 90.0 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 | °C | |
| Barrel 3 zone temperature | 220 | °C | |
| Barrel 5 zone temperature | 290 | °C | |
| Connector temperature | 290 | °C | |
| Nozzle temperature | 290 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 20 in/min |
| 4. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |