| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Generic | SAN |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 220℃，10.0kg | 28 | g/10min | ISO1133 |
| 200℃，5.0kg | 3.0 | g/10min | ASTM D1238 |
| Flame retardant level | 1/16″HB | HB | |
| Density | 1.06 | ASTM D792 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 83 | M 级 | ASTM D785 |
| Tensile strength | 730 | kg/cm | ASTM D-638 |
| Bending elasticity | 3.6×10 | kg/cm | ASTM D-790 |
| bending strength | 101.043 | MPa | ASTM D790 |
| Tensile strain | 3.0 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 92 | ℃ | ASTM D648 |
| 0.45 MPa | 101 | ℃ | ASTM D648 |
| Vicat Softening Temp | 106 | ℃ |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 3.2mm | 2.0 | kg.cm/cm | ASTM D256 |
| 6.4mm | 1.8 | kg.cm/cm | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |