EMERGE PC 4903 is a 30% glass fiber reinforced high flow ignition resistant polycarbonate resin. This resin does not contain bromine and chlorine flame retardants. EMERGE PC 4903 is designed with superior processability for use in structural parts of printers, scanners, copiers as well as internal parts for ITE applications. Applications: Structural parts of printers, scanners, and copiers Internal parts of ITE machines&& |
Product Description | |
---|---|
Supplier | Trinseo |
Generic | Polycarbonate |
Material Status | Commercial: Active |
Features | Excellent Processability,High liquidity,Halogen free,Flame Characteristics,V-0,5VA |
Availabilitys | North America,Asia Pacific |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.46 | g/cm³ | ASTM D792 |
Melt Flow Rate | |||
300℃,1.20kg | 12 | g/10min | ASTM D1238 |
Shrinkage rate | |||
MD | 0.20 to 0.40 | % | ASTM D955 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tensile modulus | 6800 | MPa | ASTM D638 |
tensile strength | |||
Yield, 3.20 mm, injection molding | 116 | MPa | ASTM D638 |
Bending modulus | |||
3.20 mm, injection molded | 8400 | MPa | ASTM D790 |
bending strength | |||
3.20 mm, injection molded | 155 | MPa | ASTM D790 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | |||
23 ℃, 3.2mm, injection molding | 130 | J/m | ASTM D256 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed | 100 | ℃ | ASTM D648 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | UL 94 | ||
1.00 mm | V-0 | UL 94 | |
2.00 mm | 5VA | UL 94 |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 110 | °C | |
Drying time | 6.0 to 8.0 | hr | |
Barrel rear temperature | 250 to 260 | °C | |
Barrel middle temperature | 260 to 270 | °C | |
Barrel front temperature | 260 to 280 | °C | |
Nozzle temperature | 271 to 300 | °C | |
Mold temperature | 60 to 100 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |