| About |
|---|
| Rilsan ® HT CMFO is a polyphthalamide produced from a renewable source. This grade, designed for injection, is the less viscous one in the Rilsan® HT family. MAIN APPLICATIONS Glass fiber compound for electronics, automotive & transportation, etc. Filament.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，2.16 kg | 45.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1750 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 58.0 | MPa | |
| fracture | 55.0 | MPa | |
| Tensile strain | ISO 527-2 | ||
| yield | 5.0 | % | |
| fracture | 190 | % | |
| Bending modulus | 1800 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Renewable Carbon Conent | > 65 | % | ASTM D6866 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Melt temperature | 270 to 310 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |