| About |
|---|
| Polypropylene PPH 6088 is a homopolymer with a Melt Flow Index of 9 g/10 min for the cast extrusion of films with excellent optical properties and good sterilizability. Polypropylene PPH 6088 is formulated with slip and anti-block agents. It is recommended for food packaging, textile packaging, flowers packaging, lamination films and stationary supplies.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Smoothness,Good disinfection,Optical performance,High anti-blocking,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent density | 0.53 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | ISO 527-3 | ||
| yield | 30.0 | MPa | ISO 527-2 |
| MD, yield, 50 µ m, blow molded film | 22.0 | MPa | ISO 527-3 |
| TD, yield, 50 µ m, blow molded film | 22.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| yield | 10 | % | ISO 527-2 |
| MD, fracture, 50 µ m, cast thin film | 700 | % | ISO 527-3 |
| TD, fracture, 50 µ m, cast thin film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| 50 µ m, cast thin film | 280 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 50 µ m, cast thin film | 14 | N | ISO 6383-2 |
| TD: 50 µ m, cast thin film | 27 | N | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 152 | ℃ | ISO 306/A50 |
| B50 | 87.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 160 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, cast thin film | 89 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | 1.4 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1400 | MPa | ISO 527-2 |
| Bending modulus | 1300 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 95 | ISO 2039-2 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| MD, fracture, 50 µ m, blow molded film | 60.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 55.0 | MPa | ISO 527-3 |
| Notes |
|---|
| 1. SiO2 |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |