| Hostalen PP H2250 36 is a polypropylene homopolymer, grey colored similar to RAL 7032 (pebble grey) and is typically used by customers for the application of extruded or compression molded sheets. For further details about the suitable applications for this material please contact LyondellBasell.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Inoxidizability,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，5.0kg | 0.50 | g/10min | ISO 1133 |
| 230℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| 230℃，5.0kg | 1.3 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0℃ | 6.0 | kJ/m² | ISO 179 |
| 23℃ | 26 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 98.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 157 | ℃ | ISO 306/A50 |
| B50 | 95.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 159 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 66.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| Secant, 23 ℃ | 1500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 36.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 12 | % | ISO 527-2/50 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 280 | °C | |
| Melt temperature | 200 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |