| NORYL PX9406P resin is an FR (non-halogenated) grade potentially suitable for a variety of electronics applications. RTI (impact) = 105 C. F1 listed in BK color.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | V-0,5VA,5VB,Flame Characteristics,Halogen free |
| Availabilitys | Europe,North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 280℃，5 kg | 10.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2800 | MPa | ASTM D638 |
| Tensile modulus | 2730 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 55.0 | MPa | ISO 527-2/50 |
| yield | 76.0 | MPa | ISO 527-2/50 |
| yield | 76.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 9.4 | % | ISO 527-2/50 |
| fracture | 9.7 | % | ASTM D638 |
| yield | 4.7 | % | ISO 527-2/50 |
| yield | 4.7 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 50 mm span | 2840 | MPa | ASTM D790 |
| 6.40 mm | 2840 | MPa | ASTM D790 |
| Bending modulus | 2580 | MPa | ISO 178 |
| bending strength | 114 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 113 | MPa | ASTM D790 |
| Yield, 6.40 mm | 114 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 60 | J/m | ASTM D256 |
| 23℃ | 130 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 52.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 64 mm span | 118 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 133 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 118 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 122 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 150 | ℃ | ISO 306/A120 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Relative temperature index | |||
| static state | 110 | ℃ | UL 746 |
| Electrical performance | 110 | ℃ | UL 746 |
| Impact load | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | SABIC | |
| 2.00 mm | 5VB | SABIC | |
| 2.50 mm | 5VA | SABIC | |
| Glowing wire flammability index | |||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 750 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 775 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 243 to 293 | °C | |
| Barrel middle temperature | 254 to 299 | °C | |
| Barrel front temperature | 266 to 304 | °C | |
| Nozzle temperature | 277 to 304 | °C | |
| Processing (melt) temperature | 277 to 304 | °C | |
| Mold temperature | 71 to 99 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Vent depth | 0.038 to 0.051 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Type 1A |
| 4. at Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |