SABIC® HDPE M453SG

About
SABIC® HDPE M453SG is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties. Typical applications. SABIC® HDPE M453SG is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE M453SG is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties. Typical applications. SABIC® HDPE M453SG is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Excellent Processability,Good surface appearance,Copolymer,High density,low-temperature impact resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.953	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	4.0	g/10min	ISO 1133
190℃，5.0kg	11	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	5.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	81.0	℃	ISO 75-2/B
Vicat Softening Temp	124	℃	ISO 306/A
Melting temperature
DSC	132	℃	ISO 11357-3
Enthalpy Change	203	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	61		ISO 868
Tensile modulus
2 mm, molded into shape	1100	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	26.0	MPa	ISO 527-2/1BA/50
Fracture, 2 mm, molded	31.0	MPa	ISO 527-2/1BA/50
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1200	MPa	ISO 178
bending strength
2 mm, molded into shape	26.0	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	232 to 260	°C
Mold temperature	20 to 40	°C
Injection pressure	93.0 to 103	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.