| NYCOA 471 R is a medium viscosity Nylon 6 resin particularly suitable for extrusion processing. It possesses an excellent combination of strength, and toughness; as well as excellent heat, chemical, and abrasion resistance inherent to Nylon 6. Its high melt viscosity and strength provide ease of processing from either a flat or a circular die. Similarly, tubes, pipes, and tapes have been processed with excellent results. Injection molding of high strength parts can be accomplished with molding cycles similar to those obtained with general purpose grade resins, even though higher cylinder temperatures may sometimes be required.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High Heat Resistance,Good melt strength,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 235℃，1.0kg | 2.6 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 1.6 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 80.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 |
| Bending modulus | 2500 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 177 | ℃ | ASTM D648 |
| Melting temperature | 220 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |