| About |
|---|
| Orgalloy® LE 6000 NAT resin is a polyamide alloy especially designed for cable sheathing and blown film extrusion. This natural grade dedicated to extrusion offers excellent barrier properties and chemical resistance to hydrocarbons, alcohols and solvents. Orgalloy® LE 6000 NAT resin conforms to the European regulations concerning materials in contact with foodstuffs.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Ethanol tolerance,Food contact compliance,Block resin,Solvent resistance,Heat Stabilized,Hydrocarbons |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，2.16 kg | 3.00 | cm³/10min | |
| Shrinkage rate | |||
| TD | 0.70 | % | |
| MD | 0.80 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.4 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.8 | % | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 44.0 | MPa | |
| MD, yield | 25.0 | MPa | |
| TD, yield | 26.0 | MPa | |
| MD, fracture | 53.0 | MPa | |
| TD, fracture | 41.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| MD, yield | 20 | % | |
| TD, yield | 14 | % | |
| MD, fracture | 410 | % | |
| TD, fracture | 490 | % | |
| Drop hammer impact | 310 | g | |
| Elmandorf tear strength | |||
| MD | 25 | N | |
| TD | 150 | N | |
| Water vapor transmittance | |||
| 23℃，85% RH | 60 | g/m²/24 hr | |
| Oxygen transfer rate | |||
| 0% RH：23℃ | 90 | cm³/m²/bar/24 hr | |
| 85% RH：23℃ | 90 | cm³/m²/bar/24 hr | |
| Carbon dioxide transfer rate | |||
| 0% RH：23℃ | 290 | cm³/m²/bar/24 hr | |
| 85% RH：23℃ | 290 | cm³/m²/bar/24 hr |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 29 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 45.0 | ℃ | |
| Vicat Softening Temp | 118 | ℃ | |
| Melting temperature | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 66 | ||
| Tensile modulus | 1820 | MPa | |
| Nominal tensile fracture strain | > 50 | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |