| About |
|---|
| LOCTITE HYSOL GR 2720 is a green epoxy based molding compound designed for the encapsulation of passive components. This material is an excellent candidate for the molding of pressure sensitive components. LOCTITE HYSOL GR 2720 meets UL 94 V-0 Flammability at 6.35mm thickness. Product Benefits Green product Low stress High Tg High strength Mold at low temperatures Fast cycle time&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Quick molding cycle,Baking |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.87 | g/cm³ | |
| Spiral flow length | 96.5 | cm | |
| Shrinkage rate | |||
| MD | 0.23 | % | |
| Water absorption rate | |||
| 85℃，7days，85% RH | 0.30 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 160 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| < 160℃ | 1.8E-5 | cm/cm/℃ | |
| > 160℃ | 5.8E-5 | cm/cm/℃ | |
| Thermal conductivity coefficient | 0.70 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 25 ℃ | 3.2E+16 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 6.40 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Extractable ion content | |||
| Chloride | 5 | ppm | |
| Sodium | 2 | ppm |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Gelation time | |||
| 175℃ | 0.32 | min | |
| Storage period | |||
| -18℃ | 6 | month |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, 175 ℃ | 90 | ||
| Bending modulus | |||
| 25℃ | 16200 | MPa | |
| bending strength | |||
| 25℃ | 157 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 347°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |