| Ethylene – Acrylic Ester – Maleic Anhydride terpolymer BONDINE® 8210 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, BONDINE® 8210 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | EAA |
| Material Status | Commercial: Active |
| Features | High pressure heat resistance,Terpolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ISO 1183 , ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 200 | g/10min | ASTM D1238，ISO 1133 |
| Ethyl acrylate content | 6.5 | wt% | Internal Method |
| Maleic anhydride content | 2.8 | wt% | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 57.0 | ℃ | ISO 306/A , ASTM D1525 3 |
| Melting temperature | 100 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 26 | ASTM D2240 , ISO 868 | |
| tensile strength | |||
| Fracture, molded | 6.00 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 400 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 40.0 | MPa | ASTM D790 , ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. On Compression Molded Samples |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |