| SABIC® HDPE M200056 SABIC® HDPE M200056 is a high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It is typically used for easy mold fill-out and low warpage with a good balance of toughness and stiffness characteristics. Typical applications. SABIC® HDPE M200056 is typically used for injection moulding of food containers, housewares, toys, base cups, caps and closures. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&SABIC® HDPE M200056 M200056 is High Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to give good flow properties, low warpage with good dimensional stability and high gloss. Typical Applications M200056 is recommended for houseware, food containers, toys, caps and closures etc.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Low warping,Excellent Processability,Good surface appearance,Good Dimensional Stability,Good liquidity,Food contact compliance,Weight distribution,Copolymer,High density |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 60 ℃, 3.00 mm, detergent, molded | 60.0 | hr | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, molded | 3.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 128 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 132 | ℃ | ISO 11357-3 |
| Enthalpy Change | 210 | J/g | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 62 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1200 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ASTM D638 | ||
| Yield, 2 mm, molded | 28.0 | MPa | |
| Fracture, 2 mm, molded | 15.0 | MPa | |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 200 | % | ASTM D638 |
| Bending modulus | |||
| 2 mm, molded into shape | 1350 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 28.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 250 | °C | |
| Mold temperature | 15.0 to 60.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |