Fire resistance PC/PBT alloy Pamphleti The P0lycarbonate(PC) material has good impact strength, surface glossiness and self-extinguishing, but its fluidity and anti—environmental stress are very poor. The Polyethylene terephthalate (PBT) has good processability and electrical property. The PC/PBT alloy has both advantages rolled into one. High fire resistant PC/PBT alloy has reached UL-94 V-0(O.8mm) and 5VA(2.5mm), and it satisfies the European Commission ROHS. The material has been recognized by multinational electronics operation and listed as one of the company global purchase items. The material can be used to electronic parts, apparatus shell.&&

About

Fire resistance PC/PBT alloy Pamphleti The P0lycarbonate(PC) material has good impact strength, surface glossiness and self-extinguishing, but its fluidity and anti—environmental stress are very poor. The Polyethylene terephthalate (PBT) has good processability and electrical property. The PC/PBT alloy has both advantages rolled into one. High fire resistant PC/PBT alloy has reached UL-94 V-0(O.8mm) and 5VA(2.5mm), and it satisfies the European Commission ROHS. The material has been recognized by multinational electronics operation and listed as one of the company global purchase items. The material can be used to electronic parts, apparatus shell.&&

Product Description
Supplier	Lihan
Generic	PC+PBT
Material Status	Commercial: Active
Features	Excellent Processability,Good surface appearance,High impact resistance,Good Electrical Properties,Flame Characteristics,Self-extinguishing,V-0,5VA
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	12	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
Melting temperature	220	℃	DSC

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+15	ohms	ASTM D257

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
0.80 mm	V-0	UL 94
2.50 mm	5VA	UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	115		ISO 2039-2
tensile strength
fracture	50.0	MPa	ISO 527-2
Tensile strain
fracture	25	%	ISO 527-2
Bending modulus	2100	MPa	ISO 178
bending strength	70.0	MPa	ISO 178

PHYSICAL	Nominal value	Unit	Test method
Density	1.29	g/cm³	ISO 1183
Shrinkage rate	0.70 to 0.90	%

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	240 to 265	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.