| About |
|---|
| Description LUTENE-H XL1800 is a optimum material for under-floor heating and tab-water pipe by RAM type extrusion. It is a excellent product with long-term internal pressure creep property and crosslinking property, mechanical properties. Applications Peroxide Crosslinked Pipes for Under-floor Heating and Drinking-water&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 2.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | 8760 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 57 | ASTM D2240 | |
| tensile strength | |||
| fracture | 3.43 | MPa | ASTM D638 |
| yield | 2.45 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 800 | % | ASTM D638 |
| Bending modulus | 981 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 123 | ℃ | ASTM D1525 4 |
| Melting temperature | 133 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |