| Pro-fax 6523 general purpose polypropylene homopolymer resin is available in pellet form. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 6523. For regulatory compliance information see Pro-fax 6523 Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat aging resistance,High ESCR,Homopolymer |
| Availabilitys | North America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.898 | g/cm³ | ASTM D792-B |
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 30.0 | MPa | ISO 527-2 |
| yield | 33.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 12 | % | ISO 527-2 |
| yield | 12 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1270 | MPa | ISO 178 |
| 1% secant | 1380 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.7 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256-A |
| 23℃ | 6.2 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 88.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 79.0 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |